ASTM B865-2020 pdf free download.Standard Specification for Precipitation Hardening Nickel-Copper-Aluminum Alloy Bar, Rod, Wire, Forgings, and Forging Stock
1. Scope
1.1 This specification covers nickel-copper-aluminum alloy (UNS N05500) in the form of rounds, squares, hexagons, or rectangles, and forgings and forging stock, manufactured either by hot working or cold working, and cold-worked wire. 1.2 The values stated in inch-pound units are to be regarded as standard, The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) for this product/material as provided by the manufacturer, to establish appropriate safety, health, and environmental practices, and determine the applicability of regulatory limitations prior to use. 1.4 This international standard was developed in accor- dance with internationally recognized principles on standard- ization established in the Decision on Principles, for the Development of International Standards, Guides and Recom- mendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
3. Terminology
3.1 Definitions of Terms Specific to This Standard: 3.1.1 bar, n- -material of rectangular (flats), hexagonal, or square solid section up to and including 10 in. (254 mm) in width and /8 in. (3.2 mm) and over in thickness in straight lengths. 3.1.2 rod, n- -material of round solid section furnished in straight lengths. 3.1.3 wire, n- a cold-worked solid product of uniform round cross section along its whole length, supplied in coil form.
4. Ordering Information
4.1 Orders for material to this specification should include the following information: 4.1.1 ASTM designation and year of issue, 4.1.2 Alloy name or UNS number (see Table 1), 4.1.3 Shape- -rod (round) or bar (square, hexagonal, or rectangular), 4.1.3.1 Forging (sketch or drawing),4.1.4 Dimensions, including length, (see Tables 2 and 3), 4.1.5 Condition (see Table 4, Table 5, and Table 6), 4.1.6 Forging stock- Specify if material is stock for reforging, 4.1.7 Finish, 4.1.8 Quantity– _feet or number of pieces, and 4.1.9 Certification- -State if certification or a report of test results is required (Section 15), 4.1.10 Samples for product (check) analysis- -State whether samples for product (check) analysis should be furnished, and 4.1.11 Purchaser inspection- -If purchaser wishes to witness tests or inspection of material at place of manufacture, the purchase order must so state indicating which test or inspec- tions are to be witnessed.
6. Mechanical Properties
6.1 Mechanical Properies- -The material in the unaged condition shall conform to the mechanical properties specified in Table 4. After aging, the material shall conform to the mechanical properties specified in Table 5 and Table 6.
7. Dimensions and Permissible Variations
7.1 Diameter, Thickness, or Width- The permissible varia- tions from the specified dimensions as measured on the diameter or between parallel surfaces of cold-worked rod and bar shall be as prescribed in Table 7; of hot-worked rod and bar as prescribed in Table 2; and of wire as prescribed in Table 7. 7.2 Out-of-Round- Hot-worked rods and cold-worked rods (except“forging quality'”) of all sizes, in straight lengths, shall not be out-of-round by more than one half the total permissible variations in diameter shown in Table 2 and Table 7, except for hot-worked rods / in. (12.7 mm) in diameter and under, which may be out-of-round by the total permissible variations in diameter shown in Table 2. Cold-worked wire shall not be out-of-round by more : than one-half the total permissible variations in diameter shown in Table 7.